Fiber orientation tensor probe XYplot: Typical fiber orientation through part thickness

[Anonymous]

I am working on a simple rectangular plate  (with short glass fiber material) example to confirm the typical fiber orientation tensor over the thickness of the part. I am running a fill pack analysis but I am getting plots like the one shown below, I know that the typical plot over the thickness should show a profile like the one in the second image. Does some have any idea why I am not getting the expected fiber orientation tensor over the thickness?

Regards,

Edgar

[mason.myers]

Hey Edgar,

Are you running a Dual Domain or 3D mesh?  Assuming you are in 3D, you could try creating a Fiber Orientation Tensor on Elements: Probe XY Plot.  That should get you the plot you need.

Mason