Hello Ivy,
When I want find a shrinkage on the part, I use the deformation result (Deflection, all effects) and I measure 2 points on the part with the button " examine results "
On the small window (of examine results), It's possible to choice "Deflection+Shrinkage".
After this, it is possible to mesure 2 points on the part several time to use an average value
if you have still some problems, I can send you a picture of shortcuts
bye.
Sebastien.
Hello Ivy,
ok,
So by default, we know (by the plastic material) the middle value indicate on the material data sheet.
Some examples:
- PA50%GF= approximatly 0.3 to 0.6%
- PP 20% mineral = approximatly 1 to 1.4%
- ABS or ASA = approximatly 0.4 to 0.6%
- TPE = approximatly 1.2 to 1.8%
Normally, if the part is not too much compacted and there is no sin mark, then the shrinkage will be OK
You will have enter an average value, because there is always a little differential shrinkage.
greeting,
Sebastien.
hi this is inba,
i understud what exactly you want.
u cant able to usnderstand about volumetric shrinkage values.
if the value is <8% - it will not impact any shink mark on the surface.
9-12%- it will create small shink mark(shallow) on the surface, but not much visible.
>13% - it will create deep visible shink mark as well as void will form on the inside of the part.
Results > New Custom Plot
DEFL Displays shrinkage and warpage with a specified magnification scale factor.
DEFL C Displays shrinkage and warpage with a specified magnification scale factor, centering the display on the node(s) specified.
DEFL W Displays warpage without shrinkage with a specified magnification scale factor, based on the position of two specified nodes.
DEFL W2 Displays warpage with uniform shrinkage, based on a specified shrinkage value.
With these u can also separate the shrinkage from the warpage.
However the results about shrinkage are reliable especcially with non filled material.
If the material is fiber filled, to obtain the correct results you have to pay attention: the shrinkage can be very different in perpendicular and parallel direction, so u have to set correctly the analysis to find out the real fibers orientation and consequently reach the right shrinkage in each direction.
Hi,
I found about this item, because we work with cosmetic plastic parts, and that is a focus of my analysis.
In the second course of Moldflow. In the manual there are a intem about the packin profile,
And this explaind a aceptable difference between 2% in all part,
Wen in a analysis a detect a difference between a area soo closed, I mension that it is a possible sink mark problem .
that because I understend if all part have a same volumetric shrinkage value, this means that all part is shrinkage equal,
but if this part have a change significant, that means that is a potensial visible spot,
The values that you expland is so interesting, because this same values was real , wen a see that values
Thatks
@Anonymous wrote:hi this is inba,
i understud what exactly you want.
u cant able to usnderstand about volumetric shrinkage values.
if the value is <8% - it will not impact any shink mark on the surface.
9-12%- it will create small shink mark(shallow) on the surface, but not much visible.
>13% - it will create deep visible shink mark as well as void will form on the inside of the part.
Hello inba,
May i ask where did you get these numbers of 8%, 13%, etc.? Ive alo used this as a reference when we design parts and they actually worked but I'd like to know how did we get this? Did Autodesk recommend this?
Eric
this is really helpful. thanks.
@Anonymous wrote:
Hello Ivy,
When I want find a shrinkage on the part, I use the deformation result (Deflection, all effects) and I measure 2 points on the part with the button " examine results "
On the small window (of examine results), It's possible to choice "Deflection+Shrinkage".
After this, it is possible to mesure 2 points on the part several time to use an average value
if you have still some problems, I can send you a picture of shortcuts
bye.
Sebastien.